The performance of water- and solvent-cast, two-component photoresist films containing poly(2-isopropenyl-2-oxazoline) or poly(2-isopropenyl-2-oxazoline-costyrene) with a photoacid generator has been investigated. These materials afford negative-tone images after deep-UV exposure and development in a suitable medium (water or toluene). Resist solutions prepared from polymers containing at least 80 mol % 2-isopropenyl-2-oxazoline may be cast from and developed in pure water. Features of higher quality can be obtained when the resist is cast from 2-methoxyethanol, probably because side reactions such as partial hydrolysis of the pendant oxazoline rings in aqueous environments are avoided. It was possible to resolve micrometer scale patterns using ca. 200 mJ/cm(2) of irradiation at 254 nm, followed by heating 2 min at 130 degrees C and development in water alone. Image quality and etch resistance were improved using copolymers containing up to 20 mol % of styrene repeat units.

Design of Photoresists with Reduced Environmental Impact. 2. Water-soluble Resists Based on Photocrosslinking of Poly(2-isopropenyl-2-oxazoline)

PASINI, DARIO;
1999-01-01

Abstract

The performance of water- and solvent-cast, two-component photoresist films containing poly(2-isopropenyl-2-oxazoline) or poly(2-isopropenyl-2-oxazoline-costyrene) with a photoacid generator has been investigated. These materials afford negative-tone images after deep-UV exposure and development in a suitable medium (water or toluene). Resist solutions prepared from polymers containing at least 80 mol % 2-isopropenyl-2-oxazoline may be cast from and developed in pure water. Features of higher quality can be obtained when the resist is cast from 2-methoxyethanol, probably because side reactions such as partial hydrolysis of the pendant oxazoline rings in aqueous environments are avoided. It was possible to resolve micrometer scale patterns using ca. 200 mJ/cm(2) of irradiation at 254 nm, followed by heating 2 min at 130 degrees C and development in water alone. Image quality and etch resistance were improved using copolymers containing up to 20 mol % of styrene repeat units.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11571/115490
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 37
  • ???jsp.display-item.citation.isi??? 37
social impact