Hybrid composite made of glauconite and polyaniline was prepared in aqueous solution of citric acid. Scanning electron microscopy combined with energy dispersive X-ray analysis shows uniform aggregates made of glauconite microparticles and polyaniline matrix. The results of X-ray powder diffraction suggest that: (1) citric acid used for the polymerisation of aniline causes formation of emeraldine salt where macromolecular ordering in the amorphous polymer takes place; (2) no chemical interaction between glauconite and emeraldine takes place in the prepared composite. FT-IR spectra of the prepared polymer and composite show features indicating all the functional groups that are present in the diiminoquinone–diaminobenzene state of polyaniline. Thermal stability of the composite was higher than the prepared polymer suggesting the occurrence of an interphase interaction between glauconite and emeraldine. After pyrolysis in purified nitrogen the composite still remained glauconite, and ε-Fe3N together with amorphous and graphitic carbon were found as reaction products. The values of electrical conductivity and magnetization of the composite suggest that optimization of these values might be achieved based upon the relationship between glauconite and polyaniline.
Properties of Glauconite/Polyaniline Composite Prepared in Aqueous Solution of Citric Acid
SALDAN, IVAN;MILANESE, CHIARA;ZEFFIRO, ALBERTO;BELLANI, VITTORIO;DI LORENZO, ROSADELE;COFRANCESCO, PACIFICO;GIRELLA, ALESSANDRO;DONDI, DANIELE;
2016-01-01
Abstract
Hybrid composite made of glauconite and polyaniline was prepared in aqueous solution of citric acid. Scanning electron microscopy combined with energy dispersive X-ray analysis shows uniform aggregates made of glauconite microparticles and polyaniline matrix. The results of X-ray powder diffraction suggest that: (1) citric acid used for the polymerisation of aniline causes formation of emeraldine salt where macromolecular ordering in the amorphous polymer takes place; (2) no chemical interaction between glauconite and emeraldine takes place in the prepared composite. FT-IR spectra of the prepared polymer and composite show features indicating all the functional groups that are present in the diiminoquinone–diaminobenzene state of polyaniline. Thermal stability of the composite was higher than the prepared polymer suggesting the occurrence of an interphase interaction between glauconite and emeraldine. After pyrolysis in purified nitrogen the composite still remained glauconite, and ε-Fe3N together with amorphous and graphitic carbon were found as reaction products. The values of electrical conductivity and magnetization of the composite suggest that optimization of these values might be achieved based upon the relationship between glauconite and polyaniline.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.