The mechanism of formation of zinc ferrite (ZnFe2O4) from ZnC2O4·1.8H2O–2FeIIC2O4·2H2O and ZnC2O4·1.8H2O–Fe2 III(C2O4)3·6H2O mixtures is investigated. By combination of TG and XRPD measurements it has been shown that microcrystalline ZnFe2O4 forms from physical mixtures after prolonged annealing at 1000 ◦C while nanocrystalline ZnFe2O4 powders are produced by mild annealing (1 h at 500 ◦C in air) of mechanically activated mixtures. The magnetic properties of ZnFe2O4 powders obtained from physical and from milled mixtures are compared.

Synthesis and magnetic properties of ZnFe2O4 obtained by mechanochemically assisted low-temperature annealing of mixtures of Zn and Fe oxalates

BERBENNI, VITTORIO;MILANESE, CHIARA;BRUNI, GIOVANNA;MARINI, AMEDEO;
2006-01-01

Abstract

The mechanism of formation of zinc ferrite (ZnFe2O4) from ZnC2O4·1.8H2O–2FeIIC2O4·2H2O and ZnC2O4·1.8H2O–Fe2 III(C2O4)3·6H2O mixtures is investigated. By combination of TG and XRPD measurements it has been shown that microcrystalline ZnFe2O4 forms from physical mixtures after prolonged annealing at 1000 ◦C while nanocrystalline ZnFe2O4 powders are produced by mild annealing (1 h at 500 ◦C in air) of mechanically activated mixtures. The magnetic properties of ZnFe2O4 powders obtained from physical and from milled mixtures are compared.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11571/132391
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 18
  • ???jsp.display-item.citation.isi??? 14
social impact