This study assessed the effect of blood contamination on the shear bond strength and bond failure site of 2 different orthodontic primers (Transbond XT and Transbond Plus Self-Etching Primer, both from 3M Unitek, Monrovia, Calif) used with adhesive-precoated brackets. Four different enamel surface conditions were tested: (1) dry, (2) blood contamination before priming, (3) blood contamination after priming, and (4) blood contamination before and after priming. Noncontaminated enamel surfaces had the highest bond strengths for both conventional and self-etching primers, which produced almost the same strength values. Under blood-contaminated conditions, both primers showed significantly reduced shear bond strengths. For the conventional primer, no significant differences were reported among the blood-contaminated groups, whereas when the self-etching primer was used, condition 4 reduced significantly the bond strength values. Significant differences in debond locations were found among the groups bonded with the 2 primers under the various enamel surface conditions.

Effect of blood contamination on shear bond strength of brackets bonded with conventional and self-etching primers

SFONDRINI, MARIA FRANCESCA;SCRIBANTE, ANDREA;
2004-01-01

Abstract

This study assessed the effect of blood contamination on the shear bond strength and bond failure site of 2 different orthodontic primers (Transbond XT and Transbond Plus Self-Etching Primer, both from 3M Unitek, Monrovia, Calif) used with adhesive-precoated brackets. Four different enamel surface conditions were tested: (1) dry, (2) blood contamination before priming, (3) blood contamination after priming, and (4) blood contamination before and after priming. Noncontaminated enamel surfaces had the highest bond strengths for both conventional and self-etching primers, which produced almost the same strength values. Under blood-contaminated conditions, both primers showed significantly reduced shear bond strengths. For the conventional primer, no significant differences were reported among the blood-contaminated groups, whereas when the self-etching primer was used, condition 4 reduced significantly the bond strength values. Significant differences in debond locations were found among the groups bonded with the 2 primers under the various enamel surface conditions.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11571/22921
Citazioni
  • ???jsp.display-item.citation.pmc??? 6
  • Scopus 37
  • ???jsp.display-item.citation.isi??? 18
social impact