Raman investigations on single crystals of K1-xLixTa1-yNbyO3 were performed to identify structural effects arising from the simultaneous presence of off-centre Li and Nb ions in the incipient ferroelectric KTaO3. Two soft-mode transitions were evidenced at 45K and 30K in a sample with x = 0.0014 and y = 0.024 after both zero-field and field cooling. These temperatures are close to the maximum and to the extrapolated Curie temperature for nonrelaxing permittivity reported in the same system. A sample with x = 0.0028 and y = 0.013 displayed a ferroelectric transition just below 30K only after field cooling, also being consistent with permittivity data.
Structural effects of Li and Nb codoping in a KTaO3 matrix: A Raman investigation
GALINETTO, PIETRO;GIULOTTO E;
2001-01-01
Abstract
Raman investigations on single crystals of K1-xLixTa1-yNbyO3 were performed to identify structural effects arising from the simultaneous presence of off-centre Li and Nb ions in the incipient ferroelectric KTaO3. Two soft-mode transitions were evidenced at 45K and 30K in a sample with x = 0.0014 and y = 0.024 after both zero-field and field cooling. These temperatures are close to the maximum and to the extrapolated Curie temperature for nonrelaxing permittivity reported in the same system. A sample with x = 0.0028 and y = 0.013 displayed a ferroelectric transition just below 30K only after field cooling, also being consistent with permittivity data.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.