Two different phosphate Nd-doped glasses have been investigated in a diode-pumped femtosecond laser. To our knowledge, only Schott’s phosphate glasses were previously used in femtosecond oscillators. A slightly different behaviour was observed in our experiments, with respect to earlier reports: clean sech2-pulses with duration <400 fs were routinely generated with wavelength corresponding to the fluorescence peak 1054 nm, whereas shorter pulses occurred at red-shifted wavelengths near 1067 nm. With a single 1-W pump diode (broad area emitter), cw slope efficiency as high as 32% and 139-fs pulse generation were demonstrated.
Phosphate Nd:glass materials for femtosecond pulse generation
AGNESI, ANTONIANGELO;CARRA', LUCA;REALI, GIANCARLO
2008-01-01
Abstract
Two different phosphate Nd-doped glasses have been investigated in a diode-pumped femtosecond laser. To our knowledge, only Schott’s phosphate glasses were previously used in femtosecond oscillators. A slightly different behaviour was observed in our experiments, with respect to earlier reports: clean sech2-pulses with duration <400 fs were routinely generated with wavelength corresponding to the fluorescence peak 1054 nm, whereas shorter pulses occurred at red-shifted wavelengths near 1067 nm. With a single 1-W pump diode (broad area emitter), cw slope efficiency as high as 32% and 139-fs pulse generation were demonstrated.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.