The aim of this study was to investigate the in vitro effect of a casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) paste (GC Tooth Mousse- TM, GC Corporation, Tokyo, Japan) on preventing enamel erosion, by using Atomic Force Microscopy (AFM). 30 human incisors, were equally assigned to 6 groups: intact enamel, enamel + soft drink, enamel + TM, enamel + TM + soft drink, enamel + soft drink + TM, enamel + soft drink + TM + soft drink. Specimens were observed through atomic force microscopy (AFM). The most common topographical parameters were determined, such as the surface roughness (Rrms ). The use of soft drink on intact enamel has roughened the surface of the sample. The application of the CPP-ACP paste on non-treated enamel made the surface smoother. A significant decrease in roughness was seen after remineralization with CPP-ACP paste. Significant differences were recorded when comparing softened enamel with softened enamel remineralized with CPP-ACP paste. Comparing eroded enamel with demineralized/remineralized specimens, the application of a CPP-ACP paste leads to a significant reduction in roughness values. AFM images of enamel surface treated with CPP-ACP resulted in less morphological changes of the tooth substrate when compared with the only eroded enamel surface morphology; thus, indicating that CPP-ACP paste promoted remineralization. Specimens' surface roughness remained similar regardless that the protective agent is used before or after exposure to coke or between two demineralizing cycles. The results confirmed the effectiveness of the CPP-ACP paste on preventing enamel erosion produced by soft drinks. SCANNING 9999:XX-XX, 2015. © 2015 Wiley Periodicals, Inc.

Protective effect of casein phosphopeptide-amorphous calcium phosphate on enamel erosion: Atomic force microscopy studies

BELTRAMI, RICCARDO;POGGIO, CLAUDIO
2015-01-01

Abstract

The aim of this study was to investigate the in vitro effect of a casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) paste (GC Tooth Mousse- TM, GC Corporation, Tokyo, Japan) on preventing enamel erosion, by using Atomic Force Microscopy (AFM). 30 human incisors, were equally assigned to 6 groups: intact enamel, enamel + soft drink, enamel + TM, enamel + TM + soft drink, enamel + soft drink + TM, enamel + soft drink + TM + soft drink. Specimens were observed through atomic force microscopy (AFM). The most common topographical parameters were determined, such as the surface roughness (Rrms ). The use of soft drink on intact enamel has roughened the surface of the sample. The application of the CPP-ACP paste on non-treated enamel made the surface smoother. A significant decrease in roughness was seen after remineralization with CPP-ACP paste. Significant differences were recorded when comparing softened enamel with softened enamel remineralized with CPP-ACP paste. Comparing eroded enamel with demineralized/remineralized specimens, the application of a CPP-ACP paste leads to a significant reduction in roughness values. AFM images of enamel surface treated with CPP-ACP resulted in less morphological changes of the tooth substrate when compared with the only eroded enamel surface morphology; thus, indicating that CPP-ACP paste promoted remineralization. Specimens' surface roughness remained similar regardless that the protective agent is used before or after exposure to coke or between two demineralizing cycles. The results confirmed the effectiveness of the CPP-ACP paste on preventing enamel erosion produced by soft drinks. SCANNING 9999:XX-XX, 2015. © 2015 Wiley Periodicals, Inc.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11571/1097935
Citazioni
  • ???jsp.display-item.citation.pmc??? 9
  • Scopus 23
  • ???jsp.display-item.citation.isi??? 17
social impact