In the present work, composite ceramics of BaTiO3 with La0.08Pb0.92Ti0.20Zr0.80O3 were prepared from powders synthesized by two different methods: (a) PLZT@BT ceramics from core-shell powders with PLZT-core and BaTiO3 shell and (b) PLZT-BT ceramic composites from mixed PLZT and BaTiO3 powders. In core-shell ceramics, a thin conductive layer of BaPbO3 was formed that resulted in an increased effective permittivity with relatively low losses (tan δ < 0.7 in kHz regions). The extrinsic contributions play an important role in both ceramics, but they are more evident in core-shell samples due to the large number of interfaces. These results show that novel functional properties can be tailored by the controlled chemical reaction at interfaces.
Tailoring the functional properties of PLZT-BaTiO3 composite ceramics by core-shell approach
MAGLIA, FILIPPO;ANSELMI TAMBURINI, UMBERTO;
2017-01-01
Abstract
In the present work, composite ceramics of BaTiO3 with La0.08Pb0.92Ti0.20Zr0.80O3 were prepared from powders synthesized by two different methods: (a) PLZT@BT ceramics from core-shell powders with PLZT-core and BaTiO3 shell and (b) PLZT-BT ceramic composites from mixed PLZT and BaTiO3 powders. In core-shell ceramics, a thin conductive layer of BaPbO3 was formed that resulted in an increased effective permittivity with relatively low losses (tan δ < 0.7 in kHz regions). The extrinsic contributions play an important role in both ceramics, but they are more evident in core-shell samples due to the large number of interfaces. These results show that novel functional properties can be tailored by the controlled chemical reaction at interfaces.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.