The possible existence of mixed methylammonium (MA)/dimethylammonium (DMA) lead bromide hybrid perovskites of general formula MA1-xDMAxPbBr3 (0 ≤ x ≤ 1) was investigated. A combined X-ray diffraction and solid-state nuclear magnetic resonance approach indicates that DMA can be incorporated up to about x = 0.30 while retaining the cubic lattice of MAPbBr3. By increasing the DMA content (x), the absorption shows a progressive blue shift and the band gap moves from about 2.17 eV (x = 0) to about 2.23 (x = 0.30) with a concomitant slightly faster recombination in the mixed cation powders.
Investigation of Dimethylammonium Solubility in MAPbBr3 Hybrid Perovskite: Synthesis, Crystal Structure, and Optical Properties
Quadrelli, Paolo;Malavasi, Lorenzo
2019-01-01
Abstract
The possible existence of mixed methylammonium (MA)/dimethylammonium (DMA) lead bromide hybrid perovskites of general formula MA1-xDMAxPbBr3 (0 ≤ x ≤ 1) was investigated. A combined X-ray diffraction and solid-state nuclear magnetic resonance approach indicates that DMA can be incorporated up to about x = 0.30 while retaining the cubic lattice of MAPbBr3. By increasing the DMA content (x), the absorption shows a progressive blue shift and the band gap moves from about 2.17 eV (x = 0) to about 2.23 (x = 0.30) with a concomitant slightly faster recombination in the mixed cation powders.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.