We investigated the flexibility of high-temperature thermal decomposition synthesis to design magnetic nanoparticles (NPs) with engineered properties. We prepared spinel iron oxide particles with the desired composition (Fe3O4 and CoFe2O4) and a well-controlled average size (5-8 nm) by tuning the synthesis procedure. The substitution of Fe by Co produces a dramatic increase of the magnetocrystalline anisotropy: for 5 nm particles, the anisotropy constant increased from ∼3.9×104 to ∼7.5×105 J/m3. The magnetocrystalline anisotropy has shown a major effect on the magnetic behavior of highly crystalline particles, except for the smallest iron oxide sample, where the surface anisotropy plays a dominant role. The presence of surfactant (oleic acid) on the NPs surface prevents direct exchange coupling among them, whereas the dipolar interaction was predominant, with an estimated temperature-equivalent energy in the range of 4-60 K.
Magnetic Interactions Versus Magnetic Anisotropy in Spinel Ferrite Nanoparticles
Lascialfari A.;
2019-01-01
Abstract
We investigated the flexibility of high-temperature thermal decomposition synthesis to design magnetic nanoparticles (NPs) with engineered properties. We prepared spinel iron oxide particles with the desired composition (Fe3O4 and CoFe2O4) and a well-controlled average size (5-8 nm) by tuning the synthesis procedure. The substitution of Fe by Co produces a dramatic increase of the magnetocrystalline anisotropy: for 5 nm particles, the anisotropy constant increased from ∼3.9×104 to ∼7.5×105 J/m3. The magnetocrystalline anisotropy has shown a major effect on the magnetic behavior of highly crystalline particles, except for the smallest iron oxide sample, where the surface anisotropy plays a dominant role. The presence of surfactant (oleic acid) on the NPs surface prevents direct exchange coupling among them, whereas the dipolar interaction was predominant, with an estimated temperature-equivalent energy in the range of 4-60 K.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.