Photoreflectance spectra of Cd(1-x)Mn(x)Te/CdTe superlattices with high compositions x = 0. 4,0. 8 were carried out at room temperature and liquid nitrogen temperature. The samples were grown by molecular beam epitaxy (MBE) technique. Exciton transitions of heavy-and light-holes related to 11H,22H,33H and 11L were observed. After taking into consideration the strain-induced and quantum confinement effects, the theoretical calculations are in very good agreement with our photo-reflectance measurement results except 33H of x = 0.8. Photoluminescence spectra were also performed at room temperature and low temperature in order to compare with our photoreflectance results.
Studies of photoreflectance spectra in Cd(1-x)Mn(x)Te/CdTe superlattices with high compositions
BELLANI, VITTORIO;GEDDO, MARIO;STELLA, ANGIOLINO;
2002-01-01
Abstract
Photoreflectance spectra of Cd(1-x)Mn(x)Te/CdTe superlattices with high compositions x = 0. 4,0. 8 were carried out at room temperature and liquid nitrogen temperature. The samples were grown by molecular beam epitaxy (MBE) technique. Exciton transitions of heavy-and light-holes related to 11H,22H,33H and 11L were observed. After taking into consideration the strain-induced and quantum confinement effects, the theoretical calculations are in very good agreement with our photo-reflectance measurement results except 33H of x = 0.8. Photoluminescence spectra were also performed at room temperature and low temperature in order to compare with our photoreflectance results.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.