Nel lavoro vengono determinati i tempi di vita radiativi e non radiativi dello ione Erbio in guide d'onda slot con strato sottile di SiO2 in un core di silicio. I risultati sono ottenuti combinando esperimenti con una trattazione teorica quantistica. The authors report a systematic study of the lifetime of the 1.54 micron transition of Er3+-doped SiO2 thin film as active material in planar slot waveguides in polycrystalline silicon. The lifetime shows a strong reduction when compared with values measured in three other configurations. The experimental results, combined with a rigorous quantum-electrodynamical formalism, are consistent with a sizable increase in both the radiative and nonradiative decay rates of Er3+ transition in slot waveguide. The radiative efficiency is only slightly reduced with respect to Er3+ in the bulk oxide, this result being important for future realization of Si-compatible active optical devices.

Modification of erbium radiative lifetime in planar silicon slot waveguides

CREATORE, CELESTINO;ANDREANI, LUCIO;
2009

Abstract

Nel lavoro vengono determinati i tempi di vita radiativi e non radiativi dello ione Erbio in guide d'onda slot con strato sottile di SiO2 in un core di silicio. I risultati sono ottenuti combinando esperimenti con una trattazione teorica quantistica. The authors report a systematic study of the lifetime of the 1.54 micron transition of Er3+-doped SiO2 thin film as active material in planar slot waveguides in polycrystalline silicon. The lifetime shows a strong reduction when compared with values measured in three other configurations. The experimental results, combined with a rigorous quantum-electrodynamical formalism, are consistent with a sizable increase in both the radiative and nonradiative decay rates of Er3+ transition in slot waveguide. The radiative efficiency is only slightly reduced with respect to Er3+ in the bulk oxide, this result being important for future realization of Si-compatible active optical devices.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11571/147990
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 26
  • ???jsp.display-item.citation.isi??? 23
social impact