IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishAc susceptibility and static magnetization measurements were performed in the optimally doped SmFeAsO0.8F0.2 superconductor. The field-temperature phase diagram of the superconducting state was drawn, and, in particular, the features of the flux lines were derived. The dependence of the intragrain depinning energy on the magnetic field intensity was derived in the thermally activated flux-creep framework, enlightening a typical 1/H dependence in the high-field regime. The intragrain critical current density was extrapolated in the zero-temperature and zero-magnetic-field limit, showing a remarkably high value Jc0(0)~2×107 A/cm2, which demonstrates that this material is rather interesting for potential future technological applications.
Scheda prodotto non validato
Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo
| Titolo: | Vortex dynamics and irreversibility line in optimally doped SmFeAsO0.8F0.2 from ac susceptibility and magnetization measurements | |
| Autori: | ||
| Data di pubblicazione: | 2011 | |
| Rivista: | ||
| Abstract: | Ac susceptibility and static magnetization measurements were performed in the optimally doped SmFeAsO0.8F0.2 superconductor. The field-temperature phase diagram of the superconducting state was drawn, and, in particular, the features of the flux lines were derived. The dependence of the intragrain depinning energy on the magnetic field intensity was derived in the thermally activated flux-creep framework, enlightening a typical 1/H dependence in the high-field regime. The intragrain critical current density was extrapolated in the zero-temperature and zero-magnetic-field limit, showing a remarkably high value Jc0(0)~2×107 A/cm2, which demonstrates that this material is rather interesting for potential future technological applications. | |