We measured photoreflectance (PR) spectra at different temperatures between 80 and 300 K, and optical absorption (OA) at 3 K on MOVPE grown Inl-xGaxAs nearly lattice-matched to InP. x-ray diffraction measurements gave a lattice mismatch δa/ao = -0.9.10−3 between ternary alloy and InP, corresponding to × = 0.485. We obtained the energy gap dependence on T from PR spectra. The blue shift of the gap was accounted for in terms of compositional difference with respect to the perfectly lattice matched alloy (× = 0.472), and elastic strain; moreover PR and OA showed evidence of the valence bands splitting at k = 0 due to interfacial strain, in fine agreement with theory.
Photoreflectance Characterization of InGaAs Lattice Matched to InP
BELLANI, VITTORIO;GEDDO, MARIO;GUIZZETTI, GIORGIO;
1994-01-01
Abstract
We measured photoreflectance (PR) spectra at different temperatures between 80 and 300 K, and optical absorption (OA) at 3 K on MOVPE grown Inl-xGaxAs nearly lattice-matched to InP. x-ray diffraction measurements gave a lattice mismatch δa/ao = -0.9.10−3 between ternary alloy and InP, corresponding to × = 0.485. We obtained the energy gap dependence on T from PR spectra. The blue shift of the gap was accounted for in terms of compositional difference with respect to the perfectly lattice matched alloy (× = 0.472), and elastic strain; moreover PR and OA showed evidence of the valence bands splitting at k = 0 due to interfacial strain, in fine agreement with theory.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.